Mechanical properties |
|
|
Tensile strength at yield |
ISO 527 |
97 MPa |
Elongation |
ISO 527 |
>60 % |
E-Modulus of tensile elasticity |
ISO 527 |
3600 MPa |
Shore (A/D) or Rockwell (R/L/M) Hardness |
ISO 868, ISO 2039-2 |
M99 |
Izod notched impact strength at 23 °C |
ISO 180/1A |
6.4 KJ/m2 |
Charpy notched toughness at 23 °C |
ISO 179/1eA |
8.2 KJ/m2 |
|
|
|
Electrical properties |
|
|
Permittivity at 50 Hz |
IEC 60250 |
3.2 |
Permittivity at 1 MHz |
IEC 60250 |
3.2 |
Dielectric loss factor at 1 MHz |
IEC 60250 |
30 1E-4 |
Dielectric strength |
IEC 60243-1 |
190 kV/mm |
Thickness for dielectric strength |
|
0.05 mm |
Specific dielectric resistance |
IEC 60093 |
1014 Ωm |
CTI Tracking resistance |
IEC 60112 |
150 |
|
|
|
Thermal properties |
|
|
Thermal conductivity |
DIN 52 612 |
0.25 W/K.m |
Coefficient of transverse expansion, linear |
ISO 11359 |
47 10-6/K |
Melt or vitrification temperature |
ISO 11357 |
340 °C |
Heat distortion resistance A |
ISO 75 HDT/A (1.8 MPa) |
152 °C |
Max. short-term temperature |
|
300 °C |
max. long-term temperature |
250 °C |
|
Max. long-term temperature |
|
-65 °C |
|
|
|
Other properties |
|
|
Water absorption under regular conditions |
ISO 62 |
<0.1 % |
Water absorption in humidity |
ISO 62 |
0.5 % |
Burning behaviour according to UL 94 |
IEC 60695-11-10 |
V-0 |
UL 94 Thickness |
|
1.45 mm |
Translucence (transparent/translucent/transparent) |
|
transparent |
Thermal ageing according to UL 746 (RTI) |
Mech. W/0 Imp. |
40 000 hrs |
|
|
|
Special properties |
|
|
Proportional elongation at yield |
ISO 527 |
5 % |
Tensile creep modulus (0.5% 1000 hrs) |
ISO 899-1 |
2500 MPa |
Flexural strength |
ISO 178 |
170 MPa |
Fatigue in flexure |
ASTM D671 |
76 MPa |
Izod impact strength at 23 °C |
ISO 180/1C |
NB KJ/m2 |
Izod notched impact strength at 23 °C |
ISO 180/4A |
65 J/m |
Coefficient of slip creep compared to steel |
|
0.43 |
Wear relative to the measured unit |
|
14 (µm/km)/MPa |
Specific heat capacity |
IEC 1006 |
2.16 J/gK |
LOI Acid index |
ISO 4589 |
35 % |