Polyethyleneterephthalate

polypet
It is an unreinforced, semi-crystalline thermoplastic polyester.
Its main advantages are its great mechanical strength, excellent dimensional stability (better than POM), abrasion resistance and very good shear properties. It also has good electrical properties; it is physiologically acceptable and flame retardant. It has very low water absorption, which does not affect its mechanical and electrical properties. Its very low thermal expansion coefficient puts it among the leading thermoplastics. This material is easily glued and welded.
Material No.: 1301
Density ISO 1183: 1.40 g/cm3
Mechanical properties    
 Tensile strength at yield  ISO 527  80 MPa
 Elongation  ISO 527  70 %
 E-Modulus of tensile elasticity  ISO 527  2800 MPa
 Brinell Hardness  ISO 2039-1  150 MPa
 Brinell Hardness Number    H358/30
 Shore (A/D) or Rockwell (R/L/M) Hardness  ISO 868, ISO 2039-2  D83
     
 Electrical properties    
 Permittivity at 50 Hz  IEC 60250  3.4
 Permittivity at 1 MHz  IEC 60250  3.2
 Dielectric loss factor at 50 Hz  IEC 60250  20 E-4
 Dielectric loss factor at 1 MHz  IEC 60250  210 1E-4
 Dielectric strength  IEC 60243-1  60 kV/mm
 Specific dielectric resistance  IEC 60093  2.1014 Ωm
 Surface resistance  IEC 60093  6.10E14 Ω
 CTI Tracking resistance  IEC 60112  35
     
 Thermal properties    
 Thermal conductivity  DIN 52 612  0.24 W/K.m
 Coefficient of transverse expansion, linear  ISO 11359  70 10-6/K
 Melt or vitrification temperature  ISO 11357  255 °C
 Heat distortion resistance A  ISO 75 HDT/A (1.8 MPa)  80 °C
 Heat distortion resistance B  ISO 75 HDT/B (0.45 MPa)  115 °C
 Max. short-term temperature    180 °C
 Max. long-term temperature    100 °C
 Min. operating temperature    -50 °C
     
 Other properties    
 Water absorption under regular conditions  ISO 62  0.2 %
 Water absorption in humidity  ISO 62  0.5 %
 Burning behaviour according to UL 94  IEC 60695-11-10  HB
     
 Special properties    
 Tensile creep modulus (0.5% 1000 hrs)  ISO 899-1  20006) MPa
 Fatigue in flexure  ASTM D671  31 MPa
Izod notched impact strength at 23 °C  ISO 180/4A  20 J/m
 Coefficient of slip creep compared to steel    0.34
 Wear relative to the measured unit    10.8 (µm/km)/MPa
 Specific heat capacity  IEC 1006  1.50 J/g K
 LOI Acid index  ISO 4589  25 %
 6) Tensile creep modulus 1%/1000 hrs    